We are more than an aluminium alloy solution provider.
Do you need consumer aluminium alloy products or learn more info about aluminum alloy prices?
Temper Types Hydro\'s most common tempers for 6082 alloy are: F - As fabricated. T5 - Cooled from an elevated temperature shaping process and artificially aged. Applies to products that are not cold worked after cooling. T5511 - Cooled from an elevated
Among wrought aluminum alloys, the composition of 6082 aluminum is
Alloy 6082 is a medium strength alloy with excellent corrosion resistance. Alloy 6082 has the highest strength of the 6000 series alloy. Due to the higher strength of Alloy 6082 it has replaced Alloy 6061 in many applications. Aluminum Alloy BS L111 Alloy 6082-T6 is available in Bars and Sections. For all stock availability contact Sales
Request Quote Sponsored by Aalco - Ferrous and Non-Ferrous Metals Stockist Apr Aluminium alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys. Alloy 6082 is known as a structural
The tensile strength, yield strength, elongation, elastic modulus and hardness of the 6082 aluminum alloy obtained with the SiC p and squeeze casting were remarkably improved, and the optimal mechanical properties were obtained with a 2 wt.% SiC p, and they increased 10.73 %, 72.7 %, 193.9 %, 23.5 % and 25.2 %, respectively,
EN AW-6082 is certified for use in marine applications. Chemical composition according to EN573-3 (weight%, remainder Al) Mechanical properties according to
Products Aluminium Aluminium 6082 Aluminium 6082 Scope Aluminium 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of 6000 series alloys. Alloy 6082 is known as a structural alloy. In plate form, 6082 is the alloy most commonly used for
TECHNICAL DATA SHEET (TDS) PRODUC 6082 ALUMINUM ALLOY PLATE Aluminum alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys. It is known as a structural alloy. In plate form, Aluminum alloy 6082 is the alloy most commonly used for
Appendix 7: Mechanical Properties Data for Selected Aluminum Alloys / 399 Table A7.2 Plane-strain fracture toughness data for aluminum alloys at various test temperatures Room-temperature Fracture toughness, K 1cor K (J) a Alloy and yield strength Specimen 24 C (75 F) 196 C (320 F) 253 C (423 F) 269 C (452 F) condition MPa ksi design
Tensile Strength, Ultimate 290 MPa 42100 psi wall thickness 5 mm 310 MPa 45000 psi wall thickness 5 mm Tensile Strength, Yield 250 MPa 36300 psi wall thickness 5 mm 260 MPa 37700 psi wall thickness 5 mm Elongation at Break Get Price Aluminium Alloy - Commercial Alloy - 6082 -
Material Thickness (mm) Tensile Strength min Yield Strength min Elongation on 50mm (min) Alloy 6082 - T6 Sheet and Plate 0.2 - 3.0 Alloy 6082 T6 Sheet and Plate 3.0 - 6.0 Alloy 6082 T6 Sheet and Plate 6.0 -
Foreign. Canada: CSA 9950. France: NF A5. United Kingdom: BS lB. West Germa- ny: DIN A199.5 Chemical Composition Composition limits. 99.50 A1 min, 0.25 Si max, 0.40 Fe max, 0.05 Cu max, 0.05 Mn max, 0.05 Mg max, 0.05 V max, 0.03 max other (each) Applications Typical
Spec: BS EN 573-3:2009 Alloy 6082 Properties Spec: BS EN 485-2:2008 Plate - 6.00m to 12.5mm Spec: BS EN 485-2:2008 Plate - 12.5mm to 100.00mm Spec: BS EN 485-2:2008 Plate - 100.00mm to 150.00mm Alloy Designations Aluminium alloy 6082 also corresponds to the following standard designations and specifications but may not be a direct
Yield strength of Aluminium is 11 MPa (pure), 400 MPa (alloys). Modulus of Elasticity of Aluminium The Young’s modulus of elasticity of Aluminium is 70 GPa. Hardness of Aluminium In materials science, hardness is the ability to withstand surface indentation ( localized plastic deformation) and scratching